BAOJI HIGHSTAR TITANIUM METAL’s titanium-based platinum-plating electrode adopts a special electroplating process. It is platinum-plated on the surface of the specially-treated titanium substrate, which can be fully or partially platinum-plated, and can be platinum-plated on titanium-clad copper and other composite materials. . The surface of the product is silver-white, and has the advantages of uniform and fine coating, firm bonding, large output current and long service life. Mainly used in: electroplating, biomedical, chemical synthesis, cathodic protection and other fields.

Substrate: first grade pure titanium TA1 GR1

Working current range: <15000A/㎡

Working temperature: <85℃

Coating Metal: 99.99% Pt

Platinum content: 22.45g/㎡/μm

Platinum layer thickness: 0.1-15μm

Product shape: net, plate, tube, rod, etc.

Use environment: PH value: 0-14

Instructions for use: To prevent scratches by hard objects, take it out of the electrolytic cell when it is stopped, rinse the surface with clean water, and store it dry. The higher the current, the shorter the service life, and using it in a solution containing fluoride ions will quickly damage the electrode.

BAOJI HIGHSTAR TITANIUM METAL also produces platinum-coated titanium electrodes, which are coated at high temperature. Various shapes, platinum content is 12g/㎡/μm, platinum layer thickness is 0.2-5μm. It is mainly used in local conductive contact of titanium electrode plates in high current environment (such as: galvanized steel plate, PS plate, etc.), preparation of acid and alkaline ionized water, etc.